Physical & Thermal
Physical & Thermal |
Method | Unit | Value |
|---|---|---|---|
| Density | ISO 1183 | g/cm³ | 1,14 |
| Melting Point | DSC | ºC | 222 |
| Mold Shrinkage (average) | ISO 294-4 | % | 1,2 - 1,6 |
| Moisture Absorption (water immersion 23ºC) 24h | ISO 62 | % | 1,5 - 9,0 |
| Vicat Softening Temperature B 9,8 N | ISO 306 | ºC | 205 |
| Heat Deflection Temperature 0,45 MPa | ISO 75-2 | ºC | 170 |
| Heat Deflection Temperature 1,81 MPa | ISO 75-2 | ºC | 60 |
| Continuous Service Temperature (without load) | IEC 60216 | ºC | 80 |
| Heat Resistance - Ball Pressure test | IEC 60695-10-2 | ºC | > 165 |
Mechanical
Mechanical |
Method | Unit | Value |
|---|---|---|---|
| Tensile Strength at Yield | ISO 527 | MPa | 85 |
| Tensile Modulus | ISO 527 | MPa | 3000 |
| Tensile Strain at Yield | ISO 527 | % | 5 |
| Tensile Strain at Break | ISO 527 | % | 40 |
| Izod - Notched Impact Strength | ISO 180/A | kJ/m² | 5,5 |
| Izod - Unnotched Impact Strength | ISO 180/U | kJ/m² | NB |
Electrical & Flame Retardancy
Electrical & Flame Retardancy |
Method | Unit | Value |
|---|---|---|---|
| Comparative Tracking Index (CTI) | IEC 60112 | V | 600 |
| Volume Resistivity | IEC 60093 | Ω*cm | 1 E14 |
| Flammability 3,0 - 1,5 - 0,8 mm | UL 94 | V2 | |
| Glow Wire Flammability Index (GWT) GWFI / 2 mm | IEC 60695-2-12 | ºC | 825 |
| Glow Wire Ingnition Temperature (GWT) GWIT / 2 mm | IEC 60695-2-13 | ºC | 750 |