PA 66 30% CARBON FIBER

Physical & Thermal

Physical & Thermal	Method	Unit	Value
Density	ISO 1183	g/cm³	1,28
Melting Point	DSC	ºC	260
Mold Shrinkage (average)	ISO 294-4	%	0,2 - 0,4
Moisture Absorption (water immersion 23ºC) 24h	ISO 62	%	1,7 - 6,0
Vicat Softening Temperature B 9,8 N	ISO 306	ºC	250
Heat Deflection Temperature 0,45 MPa	ISO 75-2	ºC	260
Heat Deflection Temperature 1,81 MPa	ISO 75-2	ºC	250
Continuous Service Temperature (without load)	IEC 60216	ºC	110
Heat Resistance - Ball Pressure test	IEC 60695-10-2	ºC	> 165

Mechanical

Mechanical	Method	Unit	Value
Tensile Strength at Break	ISO 527	MPa	210
Tensile Modulus	ISO 527	MPa	20000
Tensile Strain at Break	ISO 527	%	2
Izod - Notched Impact Strength	ISO 180/A	kJ/m²	10
Izod - Unnotched Impact Strength	ISO 180/U	kJ/m²	60

Electrical & Flame Retardancy

Electrical & Flame Retardancy	Method	Unit	Value
Volume Resistivity	IEC 60093	Ω*cm	1 E3
Flammability 3,0 - 1,5 - 0,8 mm	UL 94		HB (1,6 - 1,8 mm)
Burning Rate 350 X 100 X 1 mm	FMVSS 302 ISO 3795	mm/min	BR < 100

Molding conditions (suggested)

Molding conditions (suggested)	Method	Unit	Value
Drying Temperature		ºC	85-95
Molding temperature		ºC	270-290
Mold temperature		ºC	70-90

Edizione del / Issue 30/10/2020

Le informazioni contenute in questo documento vengono fornite in buona fede e con scopo puramente indicativo da valutare attentamente in funzione delle esigenze progettuali. Prodotto non idoneo per applicazioni alimentari e/o medicali se non diversamente indicato. Non deve essere considerato in alcun caso come un vincolo contrattuale o garanzia da parte nostra, specialmente in caso di utilizzo improprio dei nostri prodotti da parte di terzi.
The information contained herein are supplied in good faith and given purely as an indication. Properties should be carefully evaluated for all projects’ requirements. Unless otherwise specified, this product is not suitable for food and/or medical application and use. They shall not be considered in any way as a formal commitment or warranty from our company, especially in case of improper use of our products from third parties.

Documentazione