Physical & Thermal
Physical & Thermal |
Method | Unit | Value |
---|---|---|---|
Density | ISO 1183 | g/cm³ | 1,62 |
Melting Point | DSC | ºC | 166 |
Mold Shrinkage (average) | ISO 294-4 | % | 1,2 - 1,6 |
Moisture Absorption (water immersion 23ºC) 24h | ISO 62 | % | 0,15 - 0,7 |
Vicat Softening Temperature B 9,8 N | ISO 306 | ºC | 155 |
Heat Deflection Temperature 0,45 MPa | ISO 75-2 | ºC | 150 |
Heat Deflection Temperature 1,81 MPa | ISO 75-2 | ºC | 145 |
Continuous Service Temperature (without load) | IEC 60216 | ºC | 80 |
Heat Resistance - Ball Pressure test | IEC 60695-10-2 | ºC | > 125 |
Mechanical
Mechanical |
Method | Unit | Value |
---|---|---|---|
Tensile Strength at Break | ISO 527 | MPa | 65 |
Tensile Modulus | ISO 527 | MPa | 4800 |
Tensile Strain at Yeld | ISO 527 | % | - |
Tensile Strain at Break | ISO 527 | % | 3 |
Izod - Notched Impact Strength | ISO 180/A | kJ/m² | 8,5 |
Izod - Unnotched Impact Strength | ISO 180/U | kJ/m² | 45 |
Electrical & Flame Retardancy
Electrical & Flame Retardancy |
Method | Unit | Value |
---|---|---|---|
Coefficient of Friction - Static | ASTM D 3702 | 0,31 | |
Coefficient of Friction - Dynamic | ASTM D 3702 | 0,29 | |
Wear Rate | ASTM D 3702 | 4 | |
Volume Resistivity | IEC 60093 | Ω*cm | 1 E14 |
Flammability 3,0 - 1,5 - 0,8 mm | UL 94 | - | |
Glow Wire Ingnition Temperature (GWT) GWIT / 2 mm | IEC 60695-2-13 | ºC | 650 |
Burning Rate 350 X 100 X 1 mm | FMVSS 302 ISO 3795 | mm/min | - |
Molding conditions (suggested)
Molding conditions (suggested) |
Method | Unit | Value |
---|---|---|---|
Drying Temperature | ºC | 80-90 | |
Molding temperature | ºC | 180-210 | |
Mold temperature | ºC | 70-90 |